Electroplating fluid with cathodic protection in an aerosol bottle.

With 500 ML of the product, it is possible to cover an area of ​​approx. 2,9 m² (taking into account the thickness of the dried coating layer of 60 µm).

ZINGA is a one-component galvanizing system that ensures long-term cathodic protection of ferrous metals.
The zinc content in the dried coating is a minimum of 96% with a zinc particle purity of 99,995% (according to ISO 3549).
The product does not contain xylene, toluene, methyl ethyl ketone or methylene chloride. The dried layer is non-toxic and can be in contact with drinking water.
The matte gray metal layer dries quickly (touch dry in 10 min at 20°C) and withstands heat up to 120°C.
The protective powder layer does not crack when the metal expands and contracts and does not peel.
ZINGA is easy to apply to ferrous metal, previously hot-dip galvanized and ZINGA coated surfaces.
Used as an alternative to hot-dip galvanizing or metallization and to strengthen and repair previously hot-dip galvanized surfaces or as a base layer in the Duplex system (ZINGA + paint).
An excellent tool for corrosion protection of hard-to-reach surfaces.

Substrate preparation:
Apply ZINGA to a clean, rough (Rz 50-70 µm – DIN4768) surface from which dirt, grease, paint, slag and salts have been removed.
ZINGA needs to make direct contact with the metal for the electrochemical reaction.
ZINGA products can be applied to rusted surfaces if all loose rust has been removed with a metal brush and the surface has been cleaned of rust dust and grease.
For cleaning, use jet cleaning with water (140 bar, 80°C) or Zingasolv (NB do not use White Spirit!).
Clean the surface to SA 2 ½ (according to ISO 8501-1) using sandblasting or blasting.
Make sure the substrate is dust free before coating.

Application:
ZINGA must be thoroughly mixed before use. Shake the bottle for at least 30 seconds after the mixing balls are released in the bottle.
For use as a stand-alone system, a dried protective layer of 120-180 µm thickness is applied to the surface of ZINGA in two layers.
The second layer is applied to the surface 1 hour after the first one becomes dry to the touch.
When used as a duplex system (ZINGA + paint), ZINGA is applied to the surface in one layer (maximum 60-80 µm thick dried protective layer).
ZINGA can be covered with most fast-drying paints (oil, tar, epoxy, polyurethane, vinyl, iron oxide and other paints).
It is recommended to let the substrate dry for up to 72 hours before repainting and to test the suitability of the paint on a small surface beforehand.
In order to prevent the base layer from reacting during repainting, you should first apply a thin layer of paint, let it dry, and then apply a paint layer of the required thickness to the surface.
ZINGA can be applied at temperatures from -10°C to 40°C with humidity up to 95%. Spray from a distance of 30 cm. More information on the technical data card.

Highly flammable. May cause long-term damage to the aquatic environment.
Keep out of reach of children and away from sources of ignition - no smoking.
Avoid inhalation of aerosol. Use in well-ventilated rooms.
Follow the instructions for use/safety requirements. Do not spray on open flame or glowing material.
The bottle is under pressure. In case of ingestion, consult a doctor immediately. Protect from direct sunlight.
Do not store above 50°C/ 122°F.

Shake the bottle strongly before use (approx. 30 seconds after the mixing balls are released).
After each use, clean the spray channel to prevent clogging.
To do this, turn the bottom of the bottle upwards and hold the spray button down until the spray channel is empty of aerosol.

Manufacturer: ZINGAMETALL Bvba Sprl, BELGIUM, www.zinga.eu